Home Casting & Forging Products Wholesale Liquid Silicone Rubber for Cement Casting Mold/Mc Silicone

Wholesale Liquid Silicone Rubber for Cement Casting Mold/Mc Silicone

Wholesale Liquid Silicone Rubber for Cement Casting Mold/Mc Silicone
Price: US $ 6.2USD/KG
Trade Terms: FOB,CFR,EXW
Min Order: 100kg
Pay Type: L/C,T/T,Western Union,Paypal
Prod Model: MC silicone
Markets: North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe
Item: RTV 2030
Color: White
Mixing Ratio: 100:2 / 100:3 / 100:4 / 100:5
Mixed Viscosity: 24000-25000 Cps ( Adjustable )
Working Time: 30-40 Mins
Curing Time: 4-6 Hours
Hardness: 28-30 Shore a
Tear Strength: 30 N/mm
Tensile Strength: 3.8 MPa
Density(g/cm3,25 Centigrade): 1.10-1.15
Material: Silicone Rubber
Appearance: Liquid

Product Description

How to make the silicone mold by pouring way?

Please feel free to send inquiry to us, we will send you the CD instruction, if you need technical support, welcome to contact me, Mrs Berry.

Brief Introduction of RTV-2 moulding&casting materials silicon rubber

RTV-2 moulding&casting materials silicon rubber is a two component material, and it consist of Part A base silicone and Part B curing agent. When the two parts mix together and pour or brush on a object, the silicone base and curing agent can cure to be a silicone mold at room temperature; And 24 hours later, the silicone mold can be released from the object, and then the silicone mold can be poured into the following material to copy: Plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...

Procedures of RTV-2 moulding&casting materials silicon rubber

1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it is will improve the replicate times of silicone mold.

Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Extensive Applications of RTV-2 moulding&casting materials silicon rubber

RTV-2 moulding&casting materials silicon rubber can be used in the duplication of cement molds, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. etc.
 Technical parameter of RTV-2 moulding&casting materials silicon rubber
Item RTV 2030
ColorLiquid white
Curing agentCA30
Mixing ratio100:2
Mixed viscosity24000 ~25 000 cps
Working time30-40 Minutes
Curing time4-6 Hours
Hardness28-30 Shore A
Tear Strength30 N/mm
Tensile Strength0.3 MPA
Relative density1.10-1.15 g/cm3
Elongation at break480%

 
 
We are manufacturer, and specialized in manufacturing different hardness, different viscosity silicone rubber series. We can offer all kinds of silicone rubber for your request! Any interesting, please feel free to contact us. Welcome to join us, We will always at your service.

Send your message to this manufacturer

  • Mingcheng Group Limited

More >

You May Like

About Us Casting & Forging Products Casting & Forging Manufacturers Hot Casting & Forging Casting & Forging News Casting & Forging Trade Shows
Site Partners Contact Us Sitemap