The Details of forged h13 tool Steel Plate Price Per Ton H-13 is chromium, molybdenum, and vanadium hot work tool steel which has high harden ability and excellent toughness, and this isdue to the fact that the material contains molybdenum and vanadium which are strengthening agents.The chromium content of H-13resists softening when at high temperatures. H-13 has a good combination of shock and abrasion resistance, and good red hardness.This material can withstand rapid cooling and it resists premature heat checking. 1. Forging: Heating for forging has to be done slowly and uniformly. Soak through at 1900°-2000°F reheat as needed,stopping work if the temperature drops below 1650°F. After forging, cool slowly in lime, mica, dry ashes or furnace.Always anneal H-13 after forging. 2. Anneal: Heat slowly to 1550°-1650°F, hold temperature until the entire mass is heated through, then cool slowlyin the furnace (40°F per hour) to about 1000°F, after this the cooling rate can be increased. Suitable precautionsmust be taken to prevent excessive carburization or decarburization. 3. Stress Relief of Unhardened Material: When desirable to relieve the strains of machining,heat slowly to 1050°-1250°F, allow to equalize, then cool in air. 4. Hardening:? Preheat: Warm slightly before charging into the preheat furnace (the furnace should be operating at 1400°-1500°F).? Harden: H13 steel has very high hardenability and should be hardened by cooling in air.Use a salt bath or controlled atmosphere furnace to minimize decarburization,or alternatively(if not available) pack hardening in spent pitch coke.he temperature used is typically 1800°-1850°F, depending on size. ? Quench: Quench in still air or dry air blast. If complicated forms are involved, an oil quench could be used.Quench part in oil and remove from bath when it just loses its color (1000°-1100°F).Finish cooling to below 150°-125°F in air, temper immediately. ? Temper: Tempering may vary with size and end use;usually performed in the range of maximum secondary hardness or higher.Double tempering is recommended. Temper° F | Rockwell "C" |
As-quenched | 48/50 |
1000 | 50/52 |
1050 | 47/49 |
1100 | 46/48 |
Available products: Round Bar, flat bar, Steel sheets, Steel Plate.Typical Chemical Analysis: * C - .32/.45 *Mo - 1.1/1.75 *P - .03 *S - .03 Max. *Si - .80/1.2 *Mg - .2/.5 *V - .8/1.2* Chemical Analysis will vary on each heat number
Markets: |
South America,Southeast Asia,Africa,Mid East |
Standard: |
GB |
Technics: |
Forged |
Application: |
Die Steel Bar |
Surface: |
Coated |
Alloy: |
Alloy |
Special Use: |
Cold Heading Steel |
YuFengSen Special Steel Co is an ISO9001 Certified company, located in Foshan, Guangdong since 2009. We have positioned ourselves as a leading manufacturer, wholeseller and exporter of a comprehensive range of steel products. We installed advanced equipments and hired a team of skilled professionals, which can ensure the steels we produce are of high quality.
The range of products comprises die steel, Hot-working die steel, forged pieces, YuFengSen SKD61 (H13ESR), Daye 521 and so on. In addition to this, we also meet the demands of spare parts like in LM-guide, ballscrew, location module, and shaft. We also provide the other services, such as steel cutting, steel metallurgical testing, forged processing, ballscrew and LM-guide processing.
Based on mutual benefit, YuFengSen steel are hot selling to America, India, Middle East and Europe. We stick to "credit, service and quality" strategy. We have received huge appreciation from our clients for our quality products, and we are committed to ensure optimum customer satisfaction. We are looking forward to build long term partnership with you!